Figure 2.8: AES Spectrum

Typical Auger-electron spectrum for Au deposited on Si{111}.
The peaks as 92 and 107 eV are from silicon; the peak at 272 eV is from carbon contamination; and the remaining peaks are from gold.

Back to the List of Figures

Back to the experimental chapter

Figure 2.1: Schematic LEED-AES retarding-field analyzer (RFA).
Figure 2.2: Schematic LEED pattern for Si{111} 1x1.
Figure 2.3: Schematic LEED pattern for Si{111}rt3*rt3-30-X.
Figure 2.4: A LEED pattern of Si{111}7*7, at 100 eV.
Figure 2.5: Schematic LEED Data Acquisition System.
Figure 2.6: Reliability-factor (R_VHT, r_ZJ, and R_P) contour plots for the surface of TB{11-20}.
Figure 2.7: Schematic AES Data Acquisition System.
Figure 2.8: Typical Auger electron spectrum for Au deposited upon a Si{111} surface.
Figure 2.9: Schematic LEED-AES Surface Analysis UHV System.