&& NiAl{110},1 0 Beam,Davis etal,Theta=0,1003,NiAl110.a 56.85 10.67 57.99 12.48 59.13 15.49 60.27 20.00 61.42 25.85 62.56 34.091003 63.70 43.12 64.84 52.97 65.98 61.66 67.12 69.28 68.26 74.82 69.41 79.791003 70.55 83.93 71.69 89.24 72.83 94.50 73.97 99.11 75.11100.00 76.26 97.391003 77.40 89.60 78.54 79.32 79.68 67.38 80.82 57.00 81.96 47.70 83.11 41.211003 84.25 35.92 85.39 32.28 86.53 28.95 87.67 26.33 88.81 23.21 89.95 20.461003 91.10 17.00 92.24 13.87 93.38 10.58 94.52 8.19 95.66 5.81 96.80 4.401003 97.95 3.33 99.09 2.88100.23 2.55101.37 2.94102.51 3.35103.65 3.821003 104.79 4.23105.94 4.82107.08 4.86108.22 4.89109.36 4.82110.50 4.831003 111.64 4.30112.79 4.31113.93 4.33115.07 4.47116.21 4.53117.35 5.431003 118.49 5.84119.63 6.97120.78 8.29121.92 10.57123.06 13.26124.20 17.711003 125.34 22.45126.48 28.22127.63 34.26128.77 40.42129.91 45.33131.05 49.251003 132.19 51.20133.33 51.61134.47 50.45135.62 48.55136.76 46.06137.90 43.791003 139.04 41.03140.18 38.54141.32 35.78142.47 33.10143.61 29.83144.75 26.861003 145.89 23.39147.03 20.17148.17 16.88149.32 14.49150.46 12.00151.60 10.221003 152.74 8.57153.88 7.52155.02 6.26156.16 5.88157.31 5.55158.45 5.841003 159.59 5.91160.73 6.66161.87 6.71163.01 7.09164.16 7.23165.30 7.621003 166.44 7.33167.58 7.69168.72 7.35169.86 7.01171.00 6.33172.15 5.951003 173.29 5.24174.43 4.89175.57 4.21176.71 4.12177.85 3.78179.00 3.431003 180.14 2.75181.28 2.74182.42 2.15183.56 1.81184.70 1.48185.84 1.481003 186.99 1.16188.13 1.19189.27 1.22190.41 1.25191.55 1.28192.69 1.311003 193.84 1.34194.98 1.73196.12 2.14197.26 2.61198.40 3.02199.54 3.771003 200.68 4.18201.83 4.95202.97 5.74204.11 7.12205.25 8.28206.39 9.791003 207.53 10.96208.68 12.40209.82 13.34210.96 14.57212.10 15.57213.24 16.871003 214.38 17.67215.53 18.73216.67 19.40217.81 19.96218.95 20.22220.09 20.611003 221.23 20.59222.37 20.61223.52 20.13224.66 19.42225.80 18.18226.94 16.751003 228.08 14.83229.22 13.16230.37 11.34231.51 10.02232.65 8.59233.79 7.611003 234.93 6.90236.07 6.55237.21 6.23238.36 6.26239.50 6.29240.64 6.421003 241.78 6.46242.92 6.84244.06 7.25245.21 7.66246.35 7.97247.49 8.361003 248.63 8.03249.77 7.69250.91 7.08252.05 6.71253.20 6.02254.34 5.681003 255.48 5.34256.62 5.24257.76 4.56258.90 4.56260.05 4.23261.19 4.241003 262.33 3.94263.47 4.31264.61 4.00265.75 4.37266.89 4.06268.04 4.431003 269.18 4.12270.32 4.49271.46 4.18272.60 4.55273.74 4.24274.89 4.611003 276.03 4.30277.17 4.67278.31 4.37279.45 4.74280.59 4.43281.74 4.801003 282.88 4.84284.02 5.24285.16 5.29286.30 5.68287.44 5.71288.58 5.741003 289.73 5.77290.87 5.80292.01 5.83293.15 5.86294.29 5.88295.43 5.881003 5 && NiAl{110},0 1 Beam,Davis etal,Theta=0,1002,NiAl110.b 56.77 71.20 57.90 62.14 59.03 53.21 60.16 44.71 61.29 36.43 62.42 29.391002 63.55 23.15 64.68 19.07 65.81 16.97 66.94 17.54 68.06 19.05 69.19 20.971002 70.32 22.00 71.45 22.04 72.58 20.71 73.71 19.22 74.84 17.85 75.97 17.661002 77.10 18.06 78.23 19.44 79.35 21.22 80.48 23.88 81.61 26.56 82.74 29.861002 83.87 33.66 85.00 38.62 86.13 43.58 87.26 49.29 88.39 55.60 89.52 62.431002 90.65 69.25 91.77 76.94 92.90 84.31 94.03 91.40 95.16 96.80 96.29100.001002 97.42 99.41 98.55 96.06 99.68 89.29100.81 81.09101.94 71.92103.06 63.391002 104.19 55.18105.32 48.23106.45 41.67107.58 35.98108.71 30.69109.84 25.831002 110.97 20.85112.10 16.69113.23 12.83114.35 9.72115.48 7.10116.61 5.371002 117.74 4.18118.87 3.66120.00 3.36121.13 3.69122.26 3.76123.39 4.121002 124.52 4.17125.65 4.47126.77 4.20127.90 4.18129.03 3.86130.16 3.821002 131.29 3.40132.42 3.39133.55 3.08134.68 3.05135.81 2.75136.94 2.851002 138.06 2.58139.19 2.88140.32 2.61141.45 2.91142.58 2.64143.71 2.941002 144.84 2.99145.97 3.34147.10 3.41148.23 4.26149.35 5.00150.48 6.421002 151.61 8.25152.74 11.02153.87 13.96155.00 17.63156.13 21.29157.26 25.581002 158.39 29.40159.52 33.42160.65 37.13161.77 40.86162.90 43.70164.03 46.301002 165.16 47.72166.29 48.41167.42 47.83168.55 46.49169.68 44.13170.81 41.791002 171.94 38.96173.06 36.49174.19 33.99175.32 32.05176.45 29.77177.58 28.021002 178.71 25.97179.84 24.39180.97 22.38182.10 20.76183.23 18.78184.35 17.321002 185.48 15.73186.61 14.66187.74 13.45188.87 12.60190.00 11.34191.13 10.411002 192.26 9.21193.39 8.40194.52 7.53195.65 7.07196.77 6.25197.90 5.701002 199.03 5.13200.16 4.77201.29 4.15202.42 4.11203.55 3.79204.68 3.771002 205.81 3.50206.94 3.80208.06 3.73209.19 4.07210.32 4.00211.45 4.311002 5 && NiAl{110},1 1 Beam,Davis etal,Theta=0,1001,NiAl110.c 56.70100.00 57.81 97.27 58.93 90.84 60.04 79.23 61.16 64.22 62.28 49.031001 63.39 38.77 64.51 31.63 65.63 27.13 66.74 23.76 67.86 21.16 68.97 19.021001 70.09 17.37 71.21 15.90 72.32 14.68 73.44 13.47 74.55 12.42 75.67 11.321001 76.79 10.39 77.90 9.47 79.02 9.00 80.13 8.68 81.25 8.68 82.37 8.901001 83.48 9.77 84.60 10.88 85.71 12.42 86.83 14.33 87.95 16.37 89.06 18.081001 90.18 19.64 91.29 20.99 92.41 22.00 93.53 22.82 94.64 23.50 95.76 23.881001 96.88 24.26 97.99 24.52 99.11 24.90100.22 25.34101.34 26.13102.46 27.751001 103.57 30.60104.69 34.39105.80 39.17106.92 44.38108.04 49.61109.15 54.271001 110.27 58.18111.38 61.12112.50 63.06113.62 63.08114.73 61.29115.85 58.021001 116.96 53.67118.08 47.42119.20 40.83120.31 34.40121.43 28.17122.54 22.011001 123.66 17.48124.78 13.88125.89 11.06127.01 9.10128.13 8.13129.24 7.721001 130.36 7.80131.47 8.12132.59 8.52133.71 8.91134.82 8.99135.94 8.791001 137.05 8.41138.17 8.03139.29 7.49140.40 7.07141.52 6.73142.63 6.521001 143.75 6.53144.87 6.83145.98 7.26147.10 7.82148.21 8.42149.33 8.811001 150.45 9.07151.56 9.24152.68 9.24153.79 9.24154.91 9.09156.03 8.881001 157.14 8.70158.26 8.50159.38 8.38160.49 8.55161.61 9.01162.72 9.581001 163.84 10.34164.96 11.03166.07 11.79167.19 12.30168.30 12.77169.42 13.041001 170.54 13.25171.65 13.25172.77 13.25173.88 13.17175.00 13.14176.12 13.141001 177.23 13.15178.35 13.23179.46 13.45180.58 13.63181.70 13.85182.81 14.031001 183.93 14.15185.04 14.12186.16 14.16187.28 14.09188.39 13.93189.51 13.721001 190.63 13.54191.74 13.34192.86 13.18193.97 12.95195.09 12.57196.21 11.981001 197.32 11.30198.44 10.39199.55 9.50200.67 8.54201.79 7.61202.90 6.561001 204.02 5.80205.13 5.04206.25 4.38207.37 3.79208.48 3.45209.60 3.081001 210.71 2.92211.83 2.84212.95 2.89214.06 2.85215.18 2.90216.29 2.861001 217.41 2.91218.53 2.87219.64 2.92220.76 2.88221.88 2.93222.99 2.891001 224.11 2.94225.22 2.91226.34 2.95227.46 2.92228.57 2.96229.69 2.931001 230.80 2.97231.92 2.94233.04 2.98234.15 2.95235.27 2.79236.38 2.581001 237.50 2.41238.62 2.20239.73 2.05240.85 1.97241.96 1.81243.08 1.601001 244.20 1.42245.31 1.22246.43 1.30247.54 1.48248.66 1.71249.78 1.891001 250.89 2.10252.01 2.11253.13 2.11254.24 2.12255.36 2.12256.47 2.131001 257.59 2.13258.71 2.14259.82 2.14260.94 2.15262.05 2.15263.17 2.161001 264.29 2.16265.40 1.96266.52 1.79267.63 1.58268.75 1.41269.87 1.221001 270.98 1.26272.10 1.22273.21 1.27274.33 1.23275.45 1.28276.56 1.241001 277.68 1.29278.79 1.25279.91 1.30281.03 1.27282.14 1.31283.26 1.281001 284.38 1.32285.49 1.29286.61 1.33287.72 1.30288.84 1.34289.96 1.301001 5 stop && Dg_Scanned 7 times, Monday,12/14/1992,02:38:51.33 && Background Subtracted && ReNormalized to 100.00 with const : 1.1405 && FilterSmoother && Dg_Scanned 8 times, Tuesday,12/8/1992,02:36:27.59 && Background Subtracted && ReNormalized to 100.00 with const : 1.1398 && FilterSmoother && Dg_Scanned 9 times, Wednesday,12/2/1992,02:34:43.61 && Background Subtracted && ReNormalized to 100.00 with const : 1.1110 && FilterSmoother